WEPMF010 Laser Treatment of Niobium Surface for SRF Aplications 2387
 
  • V. Porshyn, D. Lützenkirchen-Hecht, P. Serbun
    Bergische Universität Wuppertal, Wuppertal, Germany
  • H. Bürger, S. Soykarci
    University of Wuppertal, Wuppertal, Germany
 
  Funding: The research was funded by the German Federal Ministry of Education and Research (BMBF) under project number 05H15PXRB1.
We report on a laser surface treatment of high purity niobium (110) single crystals. Typical surface defects like scratches, pits, sharp rims and holes were eliminated by a focused pulsed ns-laser beam. A laser fluence of about 0.68 J/cm2 and 40 - 80 pulses per spot were required to induce well detectable surface modifications. The remelted surface was sufficiently smooth, but exhibited also a number of wave structures. Thus, the surface roughness slightly increased with increasing number of pulses. Finally, boiling traces and µm-deep ablation were observed and studied as well. Local field electron emission measurements showed no emission up to 700 MV/m from a moderate remelted area below the boiling point.
 
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-IPAC2018-WEPMF010  
Export • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)